PRECITE®

Preliminary

E GF 20 black (7360)

PET GF 20

PRECITE® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

NA

Impact

35kJ/m²

PRECITE® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

A3 CF 30 5 black (7488)

PA66 CF30

AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Modulus

26.000MPa

Strength

285MPa

Impact

90kJ/m²

AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

AKROMID®

C28 GF 25 FRT grey (7560)

PA-Blend

AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

135MPa

Impact

60kJ/m²

AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

AKROMID®

B28 GF 30 S3 white (8349)

PA6-I GF30

AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

Modulus

8.900MPa

Strength

150MPa

Impact

94kJ/m²

AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

AKROLOY®

PA GF 40 black (6416)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMID®

A3 1 S3 black (21002)

PA66-I

AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

C28 GFM 10/20 5 XTC black (7367)

PA66+PA6 (GF10+MD20)

AKROMID® C28 GFM 10/20 5 XTC black (7367) - 10% glass fiber and 20% mineral reinforced, easy flowing and high heat stabilised, high dimensional stability

Modulus

9.500MPa

Strength

120MPa

Impact

40kJ/m²

AKROMID® C28 GFM 10/20 5 XTC black (7367) - 10% glass fiber and 20% mineral reinforced, easy flowing and high heat stabilised, high dimensional stability

124252680

AKROMID®

Internal

S3 GF 50 1 natural (3533)PA610 GF50

AKROMID® S3 GF 50 1 natural (3533) is a 50% glass fibre reinforced, heat stabilised polyamide 6.10 with very high stiffness and strength as well as lower moisture absorption, high chemical resistance and light inherent color.

Features

heat stabilised 130
reduced moisture

Properties

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

61 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14500 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
310 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
105 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
20 kJ/m²
16 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,51 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.