Select your fitting and find the right compound for your intend
AKROMID®
A3 GF 50 6 natural (5916)
PA66 GF50
AKROMID® A3 GF 50 6 natural (5916) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, optimized for extrusion, technical parts in industrial engineering and automotive industry
17.000MPa
270MPa
105kJ/m²
AKROMID® A3 GF 50 6 natural (5916) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, optimized for extrusion, technical parts in industrial engineering and automotive industry
AKROMID®
T5 GF 40 black (6486)
PPA GF40
AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
14.500MPa
245MPa
80kJ/m²
AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
AKROMID®
A3 GF 50 HU grey (6601)
PA66 GF50
AKROMID® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry
17.000MPa
255MPa
110kJ/m²
AKROMID® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry
AKROMID®
B28 GF 33 1 GIT black (6846)
PA6 GF33
AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.
10.500MPa
190MPa
95kJ/m²
AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.
PRECITE®
P3 GF 30 LA black (6969)
PBT GF 30
PRECITE® P3 GF 30 LA black (6969) is a 30% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and toughness as well as high dimensional and chemical resistance, laser markable.
10.000MPa
145MPa
68kJ/m²
PRECITE® P3 GF 30 LA black (6969) is a 30% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and toughness as well as high dimensional and chemical resistance, laser markable.
PRECITE®
P3 ICF 30 black (6948)
PBT CF 30
PRECITE® P3 ICF 30 black (6948) - PBT, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.
23.500MPa
175MPa
50kJ/m²
PRECITE® P3 ICF 30 black (6948) - PBT, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.
PRECITE®
V GF 20 2 natural (7737)
PBT-ASA- GF 20
PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
6.500MPa
110MPa
50kJ/m²
PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
AKROTEK®
AKROTEK® PK-VM GF 10 LT schwarz (8652) is a 10% glass fibre reinforced polyketone compound with average stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. The compound can be welded via laser welding and the corresponding laserabsorbing PK-VM GF 10 black (8685). This type was developed as the successor to PK-VM GF 10 LT black (8290) and PK-VM GF 10 LT black (8529) in order to meet the requirements for a larger processing window during processing.
Features
Properties
3.500MPa
80MPa
55kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 75
ISO 11357-3
UL 94
ISO 1183
ISO 1110
ISO 294-4
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.