HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

B3 GF 40 black (6077)

PA6 GF40

AKROMIDĀ® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

205MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROLOYĀ®

PA GF 50 natural (6414)

PA66+PA6I/6T GF50

AKROLOYĀ® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

17.000MPa

Strength

275MPa

Impact

110kJ/mĀ²

AKROLOYĀ® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROLOYĀ®

PA GF 60 black (6418)

PA66+PA6I/6T GF60

AKROLOYĀ® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

PRECITEĀ®

P3 GF 30 black (6924)

PBT GF 30

PRECITEĀ® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/mĀ²

PRECITEĀ® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

AKROMIDĀ®

B3 GF 30 6 black (20009)

PA6 GF30

AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

180MPa

Impact

80kJ/mĀ²

AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

PRECITEĀ®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

AKROMIDĀ®

A28 LGF 50 9 black (7705)

PA66 LGF50

AKROMIDĀ® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/mĀ²

AKROMIDĀ® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

19101180

AKROMIDĀ®

UL

B3 GF 30 FR natural (7458)PA6 GF30 FR(40)

AKROMIDĀ® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.

Features

flame retardant

Regulatory

ul

Properties

Modulus

10.800MPa

Strength

135MPa

Impact

65kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10800 MPa
6500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
90 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
11300 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
230 MPa
155 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3 %
5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
65 kJ/mĀ²
70 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
11 kJ/mĀ²
15 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Ball pressure test

IEC 60695-10-2

> 160 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,17 10ā»ā“/K
0,97 10ā»ā“/K

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

Burning rate 5V

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
5VA Class
5VA Class

GWFI

IEC 60695-2-12

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
960 Ā°C
960 Ā°C
960 Ā°C
960 Ā°C

GWIT

IEC 60695-2-13

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
800 Ā°C
800 Ā°C
800 Ā°C
775 Ā°C

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,39 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,4 - 1,6 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1012 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1011 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

UL
3 mm
9 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

UL
1 kV

High voltage arc tracking rate (HVTR)

UL 746A

UL
0 PLC

High Volt, Low Current Arc Resistance

ASTM D495

UL
6 PLC

Rheological Properties

Flowability

AKRO

2 mm Thickness
430 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.