AKROMID®

B3 GF 35 1 natural (2465)

PA6 GF35

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 50 1 black (2387)

PA66 GF50

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 50 1 black (20008)

PA6 GF50

AKROMID® B3 GF 50 black (20008) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

17.000MPa

Strength

210MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (20008) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

PRECITE®

Preliminary

E GF 30 ECO black (8271)

PET GF30

PRECITE® E GF 30 ECO black (8271) - PET, 30% glass fiber, high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.


Modulus

10.500MPa

Strength

170MPa

Impact

45kJ/m²

PRECITE® E GF 30 ECO black (8271) - PET, 30% glass fiber, high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

AKROMID®

Preliminary

NEXT G3 GF 30 1 natural (8085)

PA6.9 GF30

AKROMID® NEXT G3 GF 30 1 natural (8085) - partly bio-based PA 6.9, low moisture absorption, increased chemical resistance.


Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/m²

AKROMID® NEXT G3 GF 30 1 natural (8085) - partly bio-based PA 6.9, low moisture absorption, increased chemical resistance.

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.


Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

AKROMID®

B3 GF 30 1 natural (2464)

PA6 GF30

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

134580

AKROLOY®

Preliminary

PARA FGF 50 1 black (8186)PARA FGF50

AKROLOY® PARA FGF 50 1 black (8186) is a 50% flat glass fiber reinforced polyarylamide. Due to the flat glass fiber, the material is characterised by significantly improved properties 90° to the flow direction as well as low warpage. Even in conditioned state, it impresses with very high stiffness and strength owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys.

Features

surface modified
low warpage
reduced moisture
easy flow
metal substitution

Properties

Modulus

19.000MPa

Strength

295MPa

Impact

75kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
19000 MPa
19000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
295 MPa
265 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,0 %
2,2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
19500 MPa
19500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
440 MPa
405 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
75 kJ/m²
75 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
22 kJ/m²
22 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties


Density

ISO 1183

23°C
1,65 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more