Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
562 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 GF 35 1 natural (2465)

PA6 GF35

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 50 1 black (2387)

PA66 GF50

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.


Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

AKROMID®

B3 GF 30 1 natural (2464)

PA6 GF30

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B28 GF 30 2 black (7059)

PA6 GF30

AKROMID® B28 GF 30 2 black (7059) - PA 6, 30% glass fiber reinforced, easy flowing, UV and heat stabilised, outdoor applications


Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

AKROMID® B28 GF 30 2 black (7059) - PA 6, 30% glass fiber reinforced, easy flowing, UV and heat stabilised, outdoor applications

AKROMID®

B3 GF 50 4 RM-M black (3221)

PA6+X GF50

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption


Modulus

16.500MPa

Strength

210MPa

Impact

75kJ/m²

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

AKROMID®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.


Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/m²

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

134581

AKROMID®

B3 GF 15 grey (6270)PA6 GF15

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

Properties

Modulus

6.000MPa

Strength

110MPa

Impact

50kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6000 MPa
3200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
110 MPa
70 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
7,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
5000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
170 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
50 kJ/m²
90 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
6 kJ/m²
10 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 2,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.