AKROLOYĀ®

UL

PARA GF 50 HU black (8596)

PARA GF50

AKROLOYĀ® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.700MPa

Strength

295MPa

Impact

78kJ/mĀ²

AKROLOYĀ® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMIDĀ®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(40)

AKROMIDĀ® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/mĀ²

AKROMIDĀ® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMIDĀ®

B25 GF 60 1 LA black (8281)

PA6 GF60

AKROMIDĀ® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

21.000MPa

Strength

255MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

AKROLOYĀ®

UL

PARA GF 60 HU natural (8516)

PARA GF60

AKROLOYĀ® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

300MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMIDĀ®

Preliminary

NEXT 5.10 3 GF 30 natural (8406)

PA5.10 GF30

AKROMIDĀ® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/mĀ²

AKROMIDĀ® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 natural (8085)

PA6.9 GF30

AKROMIDĀ® NEXT G3 GF 30 1 natural (8085) - partly bio-based PA 6.9, low moisture absorption, increased chemical resistance.

Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 natural (8085) - partly bio-based PA 6.9, low moisture absorption, increased chemical resistance.

AKROLOYĀ®

UL

PARA GF 60 HU black (8519)

PARA GF60

AKROLOYĀ® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

145676

AKROMIDĀ®

Internal

B3 CGM 15/20 1 black (5489)PA6 (CF15+GF20)

AKROMIDĀ® B3 CGM 15/20 1 black (5489) is a 15% carbon fibre reinforced, 20% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength. Furthermore, the material impresses with its electrical conductivity. It is therefore perfectly suitable for technical applications in the automotive industry e.g. fuel filter housing. For new projects, please refer to the successor AKROMIDĀ® CGM 15/20 1 LA black (8058).

Features

heat stabilised 130

Properties

Modulus

17.000MPa

Strength

195MPa

Impact

70kJ/mĀ²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17000 MPa
9600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
195 MPa
115 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
13500 MPa
10200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
250 MPa
180 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2 %
3,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
70 kJ/mĀ²
60 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
10 kJ/mĀ²
8 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
212 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,07 10ā»ā“/K
0,98 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,36 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more