HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
538 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

UL

B3 GF 30 FR natural (7458)

PA6 GF30 FR(40)

AKROMID® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.

Modulus

10.800MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.

AKROMID®

UL

A3 GF 30 8 HU natural (8102)

PA66 GF30

AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

AKROMID®

B28 GF 60 1 natural (4775)

PA6 GF60

AKROMID® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

Modulus

22.000MPa

Strength

260MPa

Impact

100kJ/m²

AKROMID® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

AKROMID®

A3 CGM 10/20 4 black (5870)

PA66 (CF10+GF20)

AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

Modulus

14.500MPa

Strength

190MPa

Impact

65kJ/m²

AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

PRECITE®

P3 GF 30 natural (6850)

PBT GF30

PRECITE® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/m²

PRECITE® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

AKROLOY®

PARA GF 35 FR black (7496)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

PRECITE®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/m²

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

1891077

AKROMID®

B3 GF 50 9 RM-M natural (3698)PA6 + X GF50

AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.

Features

reduced moisture
process improved

Properties

Modulus

16.000MPa

Strength

210MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
16000 MPa
13000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
210 MPa
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,2 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
17200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
330 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
70 kJ/m²
70 kJ/m²
60 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
20 kJ/m²
20 kJ/m²
16 kJ/m²
20 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
280 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
165 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,61 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.