AKROMIDĀ® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry
11.500MPa
180MPa
50kJ/mĀ²
AKROMIDĀ® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
A3 GF 50 1 natural (1259)
PA66 GF50
AKROMIDĀ® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
16.700MPa
250MPa
105kJ/mĀ²
AKROMIDĀ® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
A3 GF 60 1 black (2395)
PA66 GF60
AKROMIDĀ® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised
20.500MPa
260MPa
85kJ/mĀ²
AKROMIDĀ® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised
AKROMIDĀ®
B3 GF 35 natural (2473)
PA6 GF35
AKROMIDĀ® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
11.500MPa
195MPa
100kJ/mĀ²
AKROMIDĀ® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROLOYĀ®
PARA GF 35 FR black (7496)
PARA GF35 FR(40)
AKROLOYĀ® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
14.500MPa
190MPa
55kJ/mĀ²
AKROLOYĀ® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
AKROMIDĀ®
T5 GF 35 4 black (7692)
PPA GF35
AKROMIDĀ® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
13.500MPa
220MPa
70kJ/mĀ²
AKROMIDĀ® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
AKROMIDĀ®
T9 GF 50 black (7601)
PPA GF50
AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/mĀ²
AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
AKROMIDĀ® NEXT B3 GF 30 1 L CR natural (8312) is a PA6/PP-blend with reduced density compared to standard PA6 GF 30. With 30% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where weight reduction are required. The chemical resistance is particularly superior to calcium chloride (CaClā). The material is certified according to REDcertĀ². 35% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (ā allocation factor).
Features
Regulatory
Properties
8.800MPa
140MPa
70kJ/mĀ²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 2039-1
ISO 75
ISO 75
ISO 11357-3
ISO 11359-1/2
UL 94
IEC 60695-2-12
IEC 60695-2-13
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
IEC 60112
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.