AKROMID®

A3 GF 35 3 black (1802)

PA66 GF35

AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/m²

AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 50 1 natural (1259)

PA66 GF50

AKROMID® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 35 natural (2473)

PA6 GF35

AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 60 1 black (2395)

PA66 GF60

AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

Modulus

20.500MPa

Strength

260MPa

Impact

85kJ/m²

AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

AKROMID®

B3 GF 30 RM-M black (3016)

PA6+X GF30

AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

AKROMID®

A3 1 S3 black (2768)

PA66+PA6-I

AKROMID® A3 1 S3 black (2768) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.600MPa

Strength

68MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (2768) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

PRECITE®

P3 GF 30 black (6924)

PBT GF 30

PRECITE® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/m²

PRECITE® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

178980

AKROMID®

Internal

B3 ICF 15 black (7402)PA6 CF15

AKROMID® B3 ICF 15 black BMW (7402) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. Please refer to the product B3 ICF 15 black (7402) which is identical in composition and specification. The BMW item can only be supplied with approval from BMW for specially promoted projects.

Features

heat stabilised 130

Properties

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
5000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9000 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
200 MPa
150 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
55 kJ/m²
80 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
6 kJ/m²
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Thermal conductivity

DIN 52612

0,31 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,19 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
105 Ω
105 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more