Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
A3 GM 20/10 S1 natural (1217)
PA66-I (GF20+GB10)
AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage
6.900MPa
130MPa
80kJ/m²
AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage
AKROMID®
A3 GF 35 3 black (1802)
PA66 GF35
AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry
11.500MPa
180MPa
50kJ/m²
AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GF 60 1 black (2395)
PA66 GF60
AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised
20.500MPa
260MPa
85kJ/m²
AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised
AKROMID®
B3 GF 35 natural (2473)
PA6 GF35
AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
11.500MPa
195MPa
100kJ/m²
AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROMID®
D3 GF 30 1 black (5392)
PA612 GF30
AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
9.500MPa
180MPa
95kJ/m²
AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
AKROLOY®
PA GF 60 black (6418)
PA66+PA6I/6T GF60
AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
21.000MPa
275MPa
100kJ/m²
AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLEN®
PP LGF 40 2 black (6911)PP LGF40
AKROLEN® PP LGF 40 2 black (6911) is a polypropylene homopolymer with 40% long glass fibre reinforcement which leads to a very high stiffness and strength. The materials very good surface quality as well as the outstanding UV-stability make it the product of your choice for technical parts which are exposed to UV radiation.
Features
Properties
10.000MPa
140MPa
75kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.