AKROTEK^®

PPS GF 40 black (8609)

PPS GF40

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

16.000MPa

Strength

180MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK^®

Preliminary

PK-VM GF 15 natural (8680)

PK GF15

AKROTEK® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

AKROMID^®

A3 GF 50 4 natural (71090)

PA66 GF50

AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

18.000MPa

Strength

260MPa

Impact

110kJ/m²

AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

AKROTEK^®

Preliminary

PPS GF 30 black (8610)

PPS GF30

AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

175MPa

Impact

45kJ/m²

AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK^®

Preliminary

PK-VM GF 40 black (8687)

PK GF40

AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant

Modulus

11.000MPa

Strength

160MPa

Impact

80kJ/m²

AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant

AKROTEK^®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/m²

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROMID^®

A3 S3 natural (1176)

PA66-I

AKROMID® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/m²

AKROMID® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

1 76 77 7880

AKROMID^®

Preliminary

C3 GF 30 1 FR natural (7207)PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR natural (7207) is a 30 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable E&E applications (e.g. control cabinets) as well as for railroad applications and meets the requirements for public transportation (EN 45545-2 R22/23/24 HL3).

Features

heat stabilised 130

electrically neutral

flame retardant

easy flow

E&E

public transportation

Regulatory

Properties

Modulus

10.500MPa

Strength

150MPa

Impact

76kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

76 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

225 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

251 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa

168 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Ball pressure test

IEC 60695-10-2

> 210 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h

20.000 h

155 °C

130 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

V-0 Class

Burning rate 5V

UL 94

1,6 mm Wall thickness

3,2 mm Wall thickness

5VA Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

725 °C

775 °C

HWI

UL 746A

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

0 PLC

HAI

UL 746A

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

Protection Train

EN 45545-2

R22/R23/R24 HL3

General properties

Density

ISO 1183

23°C

1,43 g/cm³

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.

10¹² Ω x cm

Comparative tracking index

IEC 60112

Test liquid A

> 600 V

Comparative tracking index

ASTM D3638

0 PLC

Dielectric strength

IEC 60243

3 mm

24,6 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1 kV

High voltage arc tracking rate (HVTR)

UL 746A

0 PLC

High Volt, Low Current Arc Resistance

ASTM D495

6 PLC

Rheological Properties

Flowability

AKRO

2 mm Thickness

460 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

C3 GF 30 1 FR natural (7207)PA66+PA6 GF30 FR(40)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Charpy impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Ball pressure test

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

Burning rate 5V

GWFI

GWIT

HWI

HAI

Burning rate (<100 mm/min)

Protection Train

General properties

Density

Electrical Properties

Volume resistivity IEC

Comparative tracking index

Comparative tracking index

Dielectric strength

Inclined-Plane Tracking, IPT

High voltage arc tracking rate (HVTR)

High Volt, Low Current Arc Resistance

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

Find the right compound

C3 GF 30 1 FR natural (7207).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66+PA6 GF30 FR(40)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Charpy impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Ball pressure test

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

Burning rate 5V

GWFI

GWIT

HWI

HAI

Burning rate (<100 mm/min)

Protection Train

General properties

Density

Electrical Properties

Volume resistivity IEC

Comparative tracking index

Comparative tracking index

Dielectric strength

Inclined-Plane Tracking, IPT

High voltage arc tracking rate (HVTR)

High Volt, Low Current Arc Resistance

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

C3 GF 30 1 FR natural (7207)PA66+PA6 GF30 FR(40)