AKROMID^®

C3 GF 30 8 black (5657)

PA66 + PA6 GF30

AKROMID® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

Modulus

9.400MPa

Strength

190MPa

Impact

82kJ/m²

AKROMID® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

AKROTEK^®

Preliminary

PPS GF 40 black (8609)

PPS GF40

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

16.000MPa

Strength

180MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK^®

Preliminary

PPS GF 40 natural (8064)

PPS GF40

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK^®

Preliminary

PK-VM GF 10 natural (8679)

PK GF10

AKROTEK® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.600MPa

Strength

75MPa

Impact

61kJ/m²

AKROTEK® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK^®

Preliminary

PPS GF 30 black (8610)

PPS GF30

AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

175MPa

Impact

45kJ/m²

AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK^®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/m²

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROLEN^®

Preliminary

NEXT PP ICF 20 AM black (8759)

PP CF20

AKROLEN® NEXT PP ICF 20 AM black (8759) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

Modulus

8.300MPa

Strength

64MPa

Impact

AKROLEN® NEXT PP ICF 20 AM black (8759) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

1 76 77 7880

AKROMID^®

B28 GF 50 9 natural (6570)PA6 GF50

AKROMID® B28 GF 50 9 natural (6570) is a 50% glass fiber reinforced polyamide 6. It is characterised by an improved flowability and mold release compared to a standard PA 6 GF 50. Furthermore, the material impresses with its high stiffness and strength. It is therefore perfectly suitable for technical applications in industrial engineering, furniture industry and in the automotive industry.

Features

easy flow

Properties

Modulus

17.000MPa

Strength

250MPa

Impact

115kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

17000 MPa

10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

250 MPa

150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

2,8 %

4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

15000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

350 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

115 kJ/m²

120 kJ/m²

100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

22 kJ/m²

26 kJ/m²

16 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

220 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa

185 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h

20.000 h

160 °C

130 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,56 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,3 - 1,6 %

Water absorption

ISO 62

23°C, saturated

4,5 - 5,1 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.

conditioned

10¹³ Ω x cm

10¹⁰ Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.

conditioned

10¹² Ω

10¹⁰ Ω

Comparative tracking index

IEC 60112

Test liquid A

600 V

Rheological Properties

Flowability

AKRO

2 mm Thickness

540 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

B28 GF 50 9 natural (6570)PA6 GF50

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

Find the right compound

B28 GF 50 9 natural (6570).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA6 GF50

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Rheological Properties

Flowability

Do you have any questions? We are happy to help.