Description

AKROTEKĀ®

Preliminary

PK-VM GF 15 natural (8680)

PK GF15

AKROTEKĀ® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 black (8468)

PA6.9 GF30

AKROMIDĀ® NEXT G3 GF 30 1 black (8468) - PA 6.9, 30% glass fibre, low moisture absorption, increased chemical resistance, good strength, good stiffness, industrial.

Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 black (8468) - PA 6.9, 30% glass fibre, low moisture absorption, increased chemical resistance, good strength, good stiffness, industrial.

AKROMIDĀ®

Preliminary

C3 GF 30 8 black (5657)

PA66 + PA6 GF30

AKROMIDĀ® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

Modulus

9.400MPa

Strength

190MPa

Impact

82kJ/mĀ²

AKROMIDĀ® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

AKROTEKĀ®

Preliminary

PK-VM GF 20 natural (8681)

PK GF20

AKROTEKĀ® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

5.700MPa

Strength

117MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

Preliminary

PK-VM GF 10 natural (8679)

PK GF10

AKROTEKĀ® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.600MPa

Strength

75MPa

Impact

61kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

Preliminary

PK-VM GF 60 natural (8684)

PK GF60

AKROTEKĀ® PK-VM GF 60 natural (8684) - Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

17.500MPa

Strength

180MPa

Impact

70kJ/mĀ²

AKROTEKĀ® PK-VM GF 60 natural (8684) - Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

A3 S3 natural (1176)

PA66-I

AKROMIDĀ® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

176777880

AKROMIDĀ®

B28 LGF 40 1 L black (6155)PA6 + PP LGF40

AKROMIDĀ® B28 LGF 40 1 L black (6155) is an easy flowing PA6/PP-blend with reduced density compared to standard PA6 LGF 40. With 40% long glass fiber reinforcement the material is suitable for components with extraordinary high stiffness and strength even at high temperature and very high impact and notched impact strength at elevated and low temperature, where weight reduction is required at the same time. B28 LGF 40 1 L black (6155) distinguish due to isotropic mechanical properties, low shrinkage, higher heat deflection temperature and very good fatigue performance. The material has very good surface properties.

Features

reduced density

Properties

Modulus

12.000MPa

Strength

200MPa

Impact

100kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12000 MPa
9500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
2,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
220 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
100 kJ/mĀ²
80 kJ/mĀ²
80 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
35 kJ/mĀ²
35 kJ/mĀ²
35 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
190 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,12 10ā»ā“/K
0,93 10ā»ā“/K

General properties

Density

ISO 1183

23Ā°C
1,36 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,1 - 1,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
240 mm
670 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more