PK-VM GF 15 natural (8680)

PK GF15

AKROTEKĀ® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEKĀ® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/mĀ²

AKROTEKĀ® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEKĀ®

Preliminary

AM ICF 20 black (8722)

ABSCF20

AKROTEKĀ® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

Modulus

13.400MPa

Strength

100MPa

Impact

20kJ/mĀ²

AKROTEKĀ® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

AKROTEKĀ®

Preliminary

PPS GF 30 black (8610)

PPS GF30

AKROTEKĀ® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

175MPa

Impact

45kJ/mĀ²

AKROTEKĀ® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEKĀ®

Preliminary

PK-VM GF 20 natural (8681)

PK GF20

AKROTEKĀ® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

5.700MPa

Strength

117MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

Preliminary

AM ICF 20 black (8723)

ASACF20

AKROTEKĀ® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

Modulus

13.400MPa

Strength

105MPa

Impact

25kJ/mĀ²

AKROTEKĀ® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

AKROMIDĀ®

A3 S3 natural (1176)

PA66-I

AKROMIDĀ® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

176777880

AKROMIDĀ®

B3 GFM 15/25 black (1312)PA6 (GF15+MD25)

AKROMIDĀ® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability

Features

surface modified
low warpage

Properties

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
190 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
50 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
4 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
190 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
216 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 Ā°C
130 - 150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,45 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,8 %

Water absorption

ISO 62

23Ā°C, saturated
6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1012 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1015 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
400 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more