AKROTEK®

Preliminary

PK-VM GF 20 natural (8681)

PK GF20

AKROTEK® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

5.700MPa

Strength

117MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK®

Preliminary

AM ICF 20 black (8722)

ABSCF20

AKROTEK® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

Modulus

13.400MPa

Strength

100MPa

Impact

20kJ/m²

AKROTEK® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

AKROMID®

UL

A3 GF 35 1 HU natural (8418)

PA66 GF35

AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.900MPa

Strength

216MPa

Impact

NA

AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMID®

A3 GF 50 4 natural (71090)

PA66 GF50

AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

18.000MPa

Strength

260MPa

Impact

110kJ/m²

AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

AKROTEK®

Preliminary

PPS GF 40 natural (8064)

PPS GF40

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PPS GF 40 black (8609)

PPS GF40

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

16.000MPa

Strength

180MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/m²

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

175767780

AKROMID®

C3 1 S3 black (4297)PA66+PA6

AKROMID® C3 1 S3 black (4297) is an unreinforced, impact modified polyamide 6.6/6 blend. It is characterised by higher dry impact strength compared to standard polyamide 6.6/6 blends while maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.

Features

heat stabilised 130
impact modified

Properties

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2500 MPa
1100 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
65 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
25 %
> 100 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
7 kJ/m²
20 kJ/m²
6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,12 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,5 - 2,7 %

Molding shrinkage

ISO 294-4

flow
transverse
1,1 - 1,3 %
1,3 - 1,5 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more