Find the right compound
Select your fitting and find the right compound for your intend
AKROMIDĀ®
NEXT U3 ICF 20 1 black (8232)
PA11 CF20
AKROMIDĀ® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
9.300MPa
110MPa
60kJ/mĀ²
AKROMIDĀ® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
AKROMIDĀ®
NEXT G3 GF 30 1 L CR black (8314)
PA6.9 + PP GF30
AKROMIDĀ® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
8.000MPa
125MPa
65kJ/mĀ²
AKROMIDĀ® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
AKROTEKĀ®
PPS GF 30 black (8610)
PPS GF30
AKROTEKĀ® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
12.000MPa
175MPa
45kJ/mĀ²
AKROTEKĀ® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
AKROTEKĀ®
PPS CF 30 black (8612)
PPS CF30
AKROTEKĀ® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
28.000MPa
230MPa
35kJ/mĀ²
AKROTEKĀ® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
AKROMIDĀ®
B3 GF 50 black (8524)
PA6 GF50
AKROMIDĀ® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.
15.500MPa
230MPa
100kJ/mĀ²
AKROMIDĀ® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.
AKROMIDĀ®
B3 GF 30 1 grey (7574)
PA6 GF30
AKROMIDĀ® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength
9.900MPa
168MPa
NA
AKROMIDĀ® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength
AKROTEKĀ®
AM ICF 20 black (8722)
ABSCF20
AKROTEKĀ® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
13.400MPa
100MPa
20kJ/mĀ²
AKROTEKĀ® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
AKROMIDĀ®
B28 LGF 40 1 L black (6155)PA6 + PP LGF40
AKROMIDĀ® B28 LGF 40 1 L black (6155) is an easy flowing PA6/PP-blend with reduced density compared to standard PA6 LGF 40. With 40% long glass fiber reinforcement the material is suitable for components with extraordinary high stiffness and strength even at high temperature and very high impact and notched impact strength at elevated and low temperature, where weight reduction is required at the same time. B28 LGF 40 1 L black (6155) distinguish due to isotropic mechanical properties, low shrinkage, higher heat deflection temperature and very good fatigue performance. The material has very good surface properties.
Features
Properties
12.000MPa
200MPa
100kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.