PRECITEĀ®

Preliminary

P3 GF 40 natural (6943)

PBT GF 40

PRECITEĀ® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.500MPa

Strength

175MPa

Impact

70kJ/mĀ²

PRECITEĀ® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROTEKĀ®

Preliminary

PK-VM GF 40 8 black (6995)

PK GF40

AKROTEKĀ® PK-VM GF 40 8 black (6995) - Polyketon, 40% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

11.000MPa

Strength

150MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 40 8 black (6995) - Polyketon, 40% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMIDĀ®

Preliminary

B+ GF 30 6 LT black (7665)

PA6 GF30

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/mĀ²

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

AKROMIDĀ®

Preliminary

B3 1 S3 natural (8013)

PA6-I

AKROMIDĀ® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 L CI natural (8377)

PA6.9 + PP GF30

AKROMIDĀ® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

Modulus

8.000MPa

Strength

125MPa

Impact

65kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

AKROLENĀ®

Preliminary

PP ICF 30 AM black (8344)

PP CF30

AKROLENĀ® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

Modulus

12.500MPa

Strength

85MPa

Impact

50kJ/mĀ²

AKROLENĀ® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

AKROMIDĀ®

B28 GF 30 S3 black (8438)

PA6-I GF30

AKROMIDĀ® B28 GF 30 S3 black (8438) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

155MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B28 GF 30 S3 black (8438) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

174757680

AKROMIDĀ®

B3 GF 30 S1 natural (1383)PA6-I GF30

AKROMIDĀ® B3 GF 30 S1 natural (1383) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry. The material has a light inherent color.

Features

impact modified

Properties

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
4200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
125 MPa
70 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
6 %
13 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
190 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
10Ā°C | d.a.m.
-
20Ā°C | d.a.m.
-
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
110 kJ/mĀ²
135 kJ/mĀ²
112 kJ/mĀ²
117 kJ/mĀ²
117 kJ/mĀ²
115 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
10Ā°C | d.a.m.
-
20Ā°C | d.a.m.
-
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
35 kJ/mĀ²
40 kJ/mĀ²
25 kJ/mĀ²
25 kJ/mĀ²
25 kJ/mĀ²
20 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,28 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more