PK-VM GF 40 black (8687)
PK GF40
AKROTEKĀ® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant
11.000MPa
160MPa
80kJ/mĀ²
AKROTEKĀ® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant
AKROTEKĀ®
PK-VM GF 10 grey (7344)
PK GF10
AKROTEKĀ® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044
3.600MPa
65MPa
50kJ/mĀ²
AKROTEKĀ® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044
AKROMIDĀ®
NEXT U28 ICF 40 1 black (8238)
PA11 CF40
AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts
20.000MPa
190MPa
80kJ/mĀ²
AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts
AKROMIDĀ®
NEXT 5.6 3 GF 30 S3 black (8444)
PA56 GF30
AKROMIDĀ® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.
8.600MPa
180MPa
96kJ/mĀ²
AKROMIDĀ® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.
AKROMIDĀ®
NEXT G3 GF 30 1 L CR black (8314)
PA6.9 + PP GF30
AKROMIDĀ® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
8.000MPa
125MPa
65kJ/mĀ²
AKROMIDĀ® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
AKROMIDĀ®
B3 GF 35 1 HU red (8416)
PA6 GF35
AKROMIDĀ® B3 GF 35 1 HU red (8416) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
12.000MPa
190MPa
NA
AKROMIDĀ® B3 GF 35 1 HU red (8416) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
AKROMIDĀ®
A3 GF 35 1 HU natural (8418)
PA66 GF35
AKROMIDĀ® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
11.900MPa
216MPa
NA
AKROMIDĀ® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
AKROMIDĀ®
A3 GF 50 6 black (6860)PA66 GF50
AKROMIDĀ® A3 GF 50 6 black (6860) is a 50% glass fiber reinforced polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is anorganically high heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry, e.g. gearbox components.
Features
Properties
18.000MPa
250MPa
105kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.