AKROTEK®
PK-VM GF 40 black (8687)
PK GF40
AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant
11.000MPa
160MPa
80kJ/m²
AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant
AKROTEK®
PK-VM GF 10 grey (7344)
PK GF10
AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044
3.600MPa
65MPa
50kJ/m²
AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044
AKROMID®
NEXT U28 ICF 40 1 black (8238)
PA11 CF40
AKROMID® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts
20.000MPa
190MPa
80kJ/m²
AKROMID® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts
AKROMID®
NEXT 5.6 3 GF 30 S3 black (8444)
PA56 GF30
AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.
8.600MPa
180MPa
96kJ/m²
AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.
AKROMID®
NEXT G3 GF 30 1 L CR black (8314)
PA6.9 + PP GF30
AKROMID® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
8.000MPa
125MPa
65kJ/m²
AKROMID® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
AKROMID®
B3 GF 35 1 HU red (8416)
PA6 GF35
AKROMID® B3 GF 35 1 HU red (8416) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
12.000MPa
190MPa
NA
AKROMID® B3 GF 35 1 HU red (8416) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
AKROMID®
A3 GF 35 1 HU natural (8418)
PA66 GF35
AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
11.900MPa
216MPa
NA
AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
AKROMID®
B28 GF 60 9 black (4662)PA6 GF60
AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
Features
Properties
21.000MPa
250MPa
90kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.