AKROMID®

B3 ICF 40 black (5020)

PA6 CF40

AKROMID® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

30.000MPa

Strength

220MPa

Impact

60kJ/m²

AKROMID® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMID®

UL

B3 1 black (6528)

PA6

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

AKROMID®

Preliminary

B28 GF 15 natural (6940)

PA6 GF 15

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/m²

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

AKROTEK®

PK-VM GF 30 8 natural (6983)

PK GF30

AKROTEK® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

8.200MPa

Strength

130MPa

Impact

60kJ/m²

AKROTEK® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROTEK®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROMID®

A3 GF 40 1 L black (4671)

PA66+PP GF40

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

11.800MPa

Strength

170MPa

Impact

80kJ/m²

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROLOY®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/m²

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

172737480

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)PA6 (GF15+GB15) FR(40)

AKROMID® B28 GM 15/15 1 FR black (8750) is a flame retardant PA6 reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens and red phosphorus. Due to its good flowability, it is characterised by easy processability as well as good surface properties. The product is suitable for enclosure applications in the E&E industry due to its low warpage, high stiffness and strength. This grade is excellent for laser marking.

Features

flame retardant
laser markable
surface modified
low warpage
easy flow
E&E

Regulatory

ul

Properties

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8400 MPa
5200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
105 MPa
65 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,7 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
45 kJ/m²
40 kJ/m²
40 kJ/m²
35 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
102 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
775 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,44 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,65 - 0,85 %
0,75 - 0,95 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more