AKROMIDĀ®

B3 ICF 40 black (5020)

PA6 CF40

AKROMIDĀ® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

30.000MPa

Strength

220MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMIDĀ®

UL

B3 1 black (6528)

PA6

AKROMIDĀ® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

AKROMIDĀ®

Preliminary

B28 GF 15 natural (6940)

PA6 GF 15

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/mĀ²

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

AKROTEKĀ®

PK-VM GF 30 8 natural (6983)

PK GF30

AKROTEKĀ® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

8.200MPa

Strength

130MPa

Impact

60kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROTEKĀ®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEKĀ® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROMIDĀ®

A3 GF 40 1 L black (4671)

PA66+PP GF40

AKROMIDĀ® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

11.800MPa

Strength

170MPa

Impact

80kJ/mĀ²

AKROMIDĀ® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROLOYĀ®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/mĀ²

AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

172737480

AKROTEKĀ®

UL

PK-VM GF 30 7 HU black (8695)PK GF30

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) is a 30% glass fibre reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. The PK-VM GF 30 schwarz (8655) was developed as the successor to meet the requirements for a larger process window during processing.

Features

hydrolysis / chemically stabilised

Regulatory

ul

Properties

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8000 MPa
7700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
130 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,1 %
3,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
210 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
65 kJ/mĀ²
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
15 kJ/mĀ²
15 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
215 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,18 10ā»ā“/K
1,16 10ā»ā“/K

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
725 Ā°C
725 Ā°C

HWI

UL 746A

1,6 mm Wall thickness
1 PLC

General properties

Density

ISO 1183

23Ā°C
1,48 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,6 - 0,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Rheological Properties

MVR

ISO 1133

240Ā°C/2,16kg
4 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more