AKROMID®
B+ GF 30 6 LT black (7665)
PA6 GF30
High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
10.000MPa
185MPa
95kJ/m²
High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
AKROMID®
NEXT G3 GF 30 1 L CI natural (8377)
PA6.9 + PP GF30
AKROMID® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
8.000MPa
125MPa
65kJ/m²
AKROMID® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
AKROTEK®
PK-VM GF 40 black (8687)
PK GF40
AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant
11.000MPa
160MPa
80kJ/m²
AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant
AKROTEK®
AM ICF 20 black (8722)
ABSCF20
AKROTEK® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
13.400MPa
100MPa
20kJ/m²
AKROTEK® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
AKROMID®
B3 GF 50 black (8524)
PA6 GF50
AKROMID® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.
15.500MPa
230MPa
100kJ/m²
AKROMID® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.
AKROMID®
A3 GF 50 4 natural (71090)
PA66 GF50
AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free
18.000MPa
260MPa
110kJ/m²
AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free
AKROMID®
B3 GF 30 1 grey (7574)
PA6 GF30
AKROMID® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength
9.900MPa
168MPa
NA
AKROMID® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength
PRECITE®
P3 GF 15 4 natural (8429)PBT-I GF15
PRECITE®P3 GF 15 4 natur (8429) is a 15% glass fibre reinforced and hydrolysis stabilised polybutylene terephthalate (PBT). It is characterised by a good stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glycidyl methacrylate) and meets the VW-50136 standard. Furthermore, the material impresses with very good dimensional stability due to its low moisture absorption. Therefore, the material is perfectly suitable for technical precision components in applications in the automotive industry, mechanical engineering, E&E and household goods industries with increased humidity.
Features
Properties
5.000MPa
85MPa
55kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Flammability
Burning rate
UL 94
General properties
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.