AKROMIDĀ®
A3 5 black (4701)
PA66
AKROMIDĀ® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6
3.500MPa
90MPa
180kJ/mĀ²
AKROMIDĀ® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6
AKROMIDĀ®
B+ GF 30 6 LT black (7665)
PA6 GF30
High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
10.000MPa
185MPa
95kJ/mĀ²
High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
AKROLOYĀ®
PA GF 60 black (7789)
PA66+PA6I/6T GF60
AKROLOYĀ® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
21.400MPa
290MPa
100kJ/mĀ²
AKROLOYĀ® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMIDĀ®
NEXT U28 ICF 40 1 black (8238)
PA11 CF40
AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts
20.000MPa
190MPa
80kJ/mĀ²
AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts
AKROMIDĀ®
A3 GF 25 3 black (3094)
PA66 GF25
AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength
8.500MPa
160MPa
50kJ/mĀ²
AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength
AKROMIDĀ®
A3 GF 40 1 L black (4671)
PA66+PP GF40
AKROMIDĀ® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride
11.800MPa
170MPa
80kJ/mĀ²
AKROMIDĀ® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride
AKROLOYĀ®
PA GF 20 black (5485)
PA66+PA6I/6T GF20
AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.
7.000MPa
145MPa
40kJ/mĀ²
AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.
AKROMIDĀ®
B25 GF 50 LA black (8280)PA6 GF50
AKROMIDĀ® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
Features
Properties
15.500MPa
235MPa
100kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.