AKROMID®

Preliminary

NEXT G3 GF 30 1 L CR black (8314)

PA6.9 + PP GF30

AKROMID® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

Modulus

8.000MPa

Strength

125MPa

Impact

65kJ/m²

AKROMID® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

AKROMID®

Preliminary

NEXT U3 ICF 20 1 black (8232)

PA11 CF20

AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

Modulus

9.300MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

AKROMID®

B3 GF 30 8 natural (5663)

PA6 GF30

AKROMID® B3 GF 30 8 natural (5663) - PA6, 30% glass fiber, food contact, kitchen and household appliances

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 8 natural (5663) - PA6, 30% glass fiber, food contact, kitchen and household appliances

AKROLOY®

Preliminary

PA GF 40 natural (6413)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROLOY®

Preliminary

PA GF 30 black (6415)

PA66+PA6I/6T GF30

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

9.800MPa

Strength

200MPa

Impact

65kJ/m²

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROMID®

A3 GK 30 6 black (6670)

PA66 GK30

AKROMID® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

86MPa

Impact

20kJ/m²

AKROMID® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

AKROTEK®

Preliminary

PK-VM GF 15 8 black (6991)

PK GF15

AKROTEK® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

4.500MPa

Strength

95MPa

Impact

55kJ/m²

AKROTEK® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

172737480

AKROMID®

Internal

B3 ICF 15 black (7402)PA6 CF15

AKROMID® B3 ICF 15 black BMW (7402) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. Please refer to the product B3 ICF 15 black (7402) which is identical in composition and specification. The BMW item can only be supplied with approval from BMW for specially promoted projects.

Features

heat stabilised 130

Properties

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
5000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9000 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
200 MPa
150 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
55 kJ/m²
80 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
6 kJ/m²
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Thermal conductivity

DIN 52612

0,31 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,19 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
105 Ω
105 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.