AKROMID®

A3 5 black (4701)

PA66

AKROMID® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6

Modulus

3.500MPa

Strength

90MPa

Impact

180kJ/m²

AKROMID® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6

AKROMID®

Preliminary

B+ GF 30 6 LT black (7665)

PA6 GF30

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/m²

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

AKROLOY®

PA GF 60 black (7789)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

290MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID®

Preliminary

NEXT U28 ICF 40 1 black (8238)

PA11 CF40

AKROMID® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/m²

AKROMID® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

AKROMID®

A3 GF 25 3 black (3094)

PA66 GF25

AKROMID® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

Modulus

8.500MPa

Strength

160MPa

Impact

50kJ/m²

AKROMID® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

AKROMID®

A3 GF 40 1 L black (4671)

PA66+PP GF40

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

11.800MPa

Strength

170MPa

Impact

80kJ/m²

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROLOY®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/m²

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

172737480

AKROMID®

B3 GF 50 RM-M black (3146)PA6 + X GF50

AKROMID® B3 GF 50 RM-M black (3146) is a 50% glass fiber reinforced polyamide 6. The material is characterised by very high stiffness and strength as well as reduced moisture absorption. As a result, there will be less changes of the mechanical properties. Thus, the material is perfectly suitable for components in the automotive industry with demands for high dimensional stability.

Features

reduced moisture

Properties

Modulus

17.000MPa

Strength

210MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17000 MPa
12000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
210 MPa
135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,2 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
17500 MPa
13000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
320 MPa
220 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
70 kJ/m²
70 kJ/m²
60 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
20 kJ/m²
20 kJ/m²
15 kJ/m²
20 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
280 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
165 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
> 650 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
> 650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,62 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.