AKROTEKĀ®
PK-HM 8 black (6246)
PK
AKROTEKĀ® PK-HM 8 black (6246) is an unreinforced, high viscosity polyketone. The material is suitable for drinking water contact and meets the requirements according to ACS and WRAS. Moreover the material corresponds to the European food guideline EU 10/2011, but not to the American FDA 21 CFR.
1.600MPa
60MPa
180kJ/mĀ²
AKROTEKĀ® PK-HM 8 black (6246) is an unreinforced, high viscosity polyketone. The material is suitable for drinking water contact and meets the requirements according to ACS and WRAS. Moreover the material corresponds to the European food guideline EU 10/2011, but not to the American FDA 21 CFR.
AKROMIDĀ®
A3 GK 30 6 black (6670)
PA66 GK30
AKROMIDĀ® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance
4.600MPa
86MPa
20kJ/mĀ²
AKROMIDĀ® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance
AKROTEKĀ®
PK-VM GF 30 8 natural (6983)
PK GF30
AKROTEKĀ® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA
8.200MPa
130MPa
60kJ/mĀ²
AKROTEKĀ® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA
AKROMIDĀ®
B+ GF 30 6 LT black (7665)
PA6 GF30
High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
10.000MPa
185MPa
95kJ/mĀ²
High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
PRECITEĀ®
P3 GF 25 9 FR natural (8212)
PBT GF25 FR(40)
PRECITEĀ® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.
8.500MPa
123MPa
53kJ/mĀ²
PRECITEĀ® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.
AKROMIDĀ®
A3 GK 30 natural (3689)
PA66 GB30
AKROMIDĀ® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
5.000MPa
90MPa
28kJ/mĀ²
AKROMIDĀ® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
AKROMIDĀ®
S3 GF 30 4 natural (3552)
PA6.10
AKROMIDĀ® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance
8.600MPa
160MPa
110kJ/mĀ²
AKROMIDĀ® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance
AKROMIDĀ®
B3 GF 30 1 HU LA black (2862)PA6 GF30
AKROMIDĀ® B3 GF 30 1 HU LA black (2862) is a 30% glass fibre reinforced, heat ageing resistant polyamide 6 with high rigidity and strength. This UL94 HB listed grade is suitable for technical components in mechanical engineering and the automotive industry. The material is laser markable.
Features
Regulatory
Properties
10.300MPa
185MPa
95kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
UV Exposure and Water Immersion
UL 746C
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Electrical Properties
Surface resistivity
DIN EN 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.