AKROTEK®

Preliminary

PK-VM GF 40 black (8687)

PK GF40

AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant

Modulus

11.000MPa

Strength

160MPa

Impact

80kJ/m²

AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant

AKROMID®

A3 GK 30 6 black (6670)

PA66 GK30

AKROMID® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

86MPa

Impact

20kJ/m²

AKROMID® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

PRECITE®

Preliminary

E GF 20 natural (7301)

PET GF 20

PRECITE® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

145MPa

Impact

40kJ/m²

PRECITE® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

Preliminary

A3 black (7557)

PA66

AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

Modulus

3.200MPa

Strength

80MPa

Impact

180kJ/m²

AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

AKROMID®

Preliminary

NEXT 5.6 3 GF 30 S3 black (8444)

PA56 GF30

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

Modulus

8.600MPa

Strength

180MPa

Impact

96kJ/m²

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

AKROMID®

UL

A3 GF 35 1 HU natural (8418)

PA66 GF35

AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.900MPa

Strength

216MPa

Impact

NA

AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMID®

Preliminary

T5 8 black (6454)

PPA

AKROMID® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

3.800MPa

Strength

75MPa

Impact

40kJ/m²

AKROMID® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

170717280

AKROMID®

UL

NEXT S3 GF 30 1 HU black (8825)PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) is a partially biobased and heat-stabilised PA6.10. With 30% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This sustainable and UL listed grade is characterised by its low moisture absorption and high chemical resistance compared to classic PA6 and PA 6.6.

Features

Bio-based
heat stabilised 130
reduced moisture

Regulatory

ul

Properties

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

59 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8600 MPa
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
7,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
5,5 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
17 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
195 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
145 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 - 1,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,8 - 1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more