Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROLOY®

UL

PARA GF 50 HU black (8596)

PARA GF50

AKROLOY® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.700MPa

Strength

295MPa

Impact

78kJ/m²

AKROLOY® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

AKROMID®

B3 GF 30 9 black (8643)

PA6 GF30

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOY®

UL

PARA GF 60 HU natural (8516)

PARA GF60

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

300MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROLOY®

UL

PARA GF 60 HU black (8519)

PARA GF60

AKROLOY® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

310MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

UL
Preliminary

B28 GF 25 9 FR orange (8644)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROMID®

A3 GM 20/10 S1 natural (1217)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

167880

AKROMID®

A3 GF 25 FR natural (7649)PA66 GF25 FR(40)

AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

Properties

Modulus

9.200MPa

Strength

135MPa

Impact

63kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9200 MPa
5800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
90 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
63 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 °C
725 °C
750 °C

General properties

Density

ISO 1183

23°C
1,37 g/cm³

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.