Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/m²

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

B3 GF 30 9 black (8643)

PA6 GF30

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOY®

UL

PARA GF 60 HU natural (8516)

PARA GF60

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

300MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

B25 GF 60 1 LA black (8281)

PA6 GF60

AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

21.000MPa

Strength

255MPa

Impact

95kJ/m²

AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

AKROMID®

UL
Preliminary

B28 GF 25 9 FR orange (8644)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROMID®

A3 GM 20/10 S1 natural (1217)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

167880

AKROMID®

Internal

A3 K6 FR blue (6752)PA66 GF30 FR(40)

AKROMID® A3 K6 FR blue (6752) is a 30% glass fibre reinforced and flame retardant PA 6.6. colored in blue similar RAL 5015. The flame retardant system is free of halogens and red phosphorus. Due to its high stiffness and strength, the material is suitable for circuit breaker and housings in E&E industry.

Features

flame retardant
E&E

Properties

Modulus

10.500MPa

Strength

120MPa

Impact

Na

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
2 %

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

3,2 mm Wall thickness
775 °C

Oxygen index

ISO 4589-2

> 32 %

General properties

Density

ISO 1183

23°C
1,43 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,4 %
0,9 - 1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more