AKROLOY®

UL

PARA GF 50 HU black (8596)

PARA GF50

AKROLOY® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.700MPa

Strength

295MPa

Impact

78kJ/m²

AKROLOY® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

AKROMID®

B3 GF 30 9 black (8643)

PA6 GF30

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOY®

UL

PARA GF 60 HU natural (8516)

PARA GF60

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

300MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROLOY®

UL

PARA GF 60 HU black (8519)

PARA GF60

AKROLOY® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

310MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

UL
Preliminary

B28 GF 25 9 FR orange (8644)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROMID®

A3 GM 20/10 S1 natural (1217)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

167880

AKROMID®

UL

A3 1 FR black (3051)PA66 FR(30)

AKROMID® A3 1 FR black (3051) is an unreinforced, flame retardant and heat stabilised PA6.6. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for switches, housing and fasteners in the electric industry.

Features

heat stabilised 130
flame retardant
E&E

Regulatory

ul

Properties

Modulus

3.500MPa

Strength

83MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3500 MPa
1500 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
83 MPa
55 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 5 %
> 20 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
70
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
4,5 kJ/m²
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
80 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
UL
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 °C
750 °C
750 °C
775 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
4 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Oxygen index

ISO 4589-2

> 32 %

General properties

Density

ISO 1183

23°C
1,18 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,6 %
1,3 - 1,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more