Find the right compound
Select your fitting and find the right compound for your intend
AKROLOYĀ®
PARA GF 60 HU black (8519)
PARA GF60
AKROLOYĀ® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute
24.000MPa
310MPa
80kJ/mĀ²
AKROLOYĀ® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute
AKROLOYĀ®
PARA GF 50 HU black (8596)
PARA GF50
AKROLOYĀ® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute
19.700MPa
295MPa
78kJ/mĀ²
AKROLOYĀ® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute
AKROMIDĀ®
B28 GF 25 9 FR orange (8644)
PA6 GF25 FR(40)
AKROMIDĀ® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.
9.000MPa
135MPa
81kJ/mĀ²
AKROMIDĀ® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.
AKROMIDĀ®
B25 GF 60 1 LA black (8281)
PA6 GF60
AKROMIDĀ® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
21.000MPa
255MPa
95kJ/mĀ²
AKROMIDĀ® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
AKROMIDĀ®
B28 GF 30 9 FR grey (8505)
PA6 GF30 FR(40)
AKROMIDĀ® B28 GF 30 9 FR grey (8505) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, grey, e-mobility.
11.000MPa
135MPa
80kJ/mĀ²
AKROMIDĀ® B28 GF 30 9 FR grey (8505) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, grey, e-mobility.
AKROLOYĀ®
PARA GF 60 HU natural (8516)
PARA GF60
AKROLOYĀ® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute
24.000MPa
300MPa
80kJ/mĀ²
AKROLOYĀ® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute
AKROMIDĀ®
A3 GM 20/10 S1 natural (1217)
PA66-I (GF20+GB10)
AKROMIDĀ® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage
6.900MPa
130MPa
80kJ/mĀ²
AKROMIDĀ® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage
AKROMIDĀ®
A3 GF 35 1 black (2269)PA66 GF35
AKROMIDĀ® A3 GF 35 1 black (2269) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.
Features
Properties
11.600MPa
215MPa
92kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Temperature index for 50% loss of tensile strength
IEC 60216
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.