AKROMID^®

NEXT 5.10 3 GF 30 natural (8406)

PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/m²

AKROMID® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

AKROMID^®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

AKROMID^®

Preliminary

B28 GF 25 9 FR orange (8644)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROMID^®

B3 GF 30 9 black (8643)

PA6 GF30

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOY^®

PARA GF 60 HU natural (8516)

PARA GF60

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

300MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROLOY^®

PARA GF 60 HU black (8519)

PARA GF60

AKROLOY® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

310MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID^®

A3 GF 50 1 natural (1259)

PA66 GF50

AKROMID® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

1 6 7 880

AKROMID^®

A3 1 S3 black (1139)PA66-I

AKROMID® A3 1 S3 black (1139) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength whilst maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry. Its good flowability qualifies the material for processing in multi-cavity moulds. For new projects, please consider our successor grade A3 1 S3 schwarz (11392).

Features

heat stabilised 130

impact modified

Properties

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

2700 MPa

1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.

50 mm/min | conditioned

63 MPa

45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.

50 mm/min | conditioned

5,6 %

> 20 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.

50 mm/min | conditioned

> 35 %

> 100 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

90 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

7,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

30°C | conditioned

no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

30°C | conditioned

17 kJ/m²

95 kJ/m²

10 kJ/m²

13 kJ/m²

Izod notched impact strength

ISO 180/1A

23°C | d.a.m.

20°C | d.a.m.

40°C | d.a.m.

15 kJ/m²

12 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

213 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,87 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness

HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness

650 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness

675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

2,0 - 2,2 %

Molding shrinkage

ISO 294-4

flow

transverse

1,3 - 1,5 %

1,5 - 1,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.

10¹⁵ Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.

10¹⁴ Ω

Comparative tracking index

IEC 60112

Test liquid A

600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

A3 1 S3 black (1139)PA66-I

Mechanical Properties

Tensile modulus

Tensile stress at yield

Tensile strain at yield

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Izod notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

GWFI

GWIT

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Do you have any questions? We are happy to help.

Find the right compound

A3 1 S3 black (1139).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66-I

Mechanical Properties

Tensile modulus

Tensile stress at yield

Tensile strain at yield

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Izod notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

GWFI

GWIT

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Do you have any questions? We are happy to help.

A3 1 S3 black (1139)PA66-I