AKROTEK® PK-VM GF 20 8 natural (6982) is a 20% glass fibre reinforced, low viscous polyketone with average stiffness and strength and light inherent color. Please note that the material is NOT suitable anymore for drinking water contact and does NOT meet the requirements according to KTW, DVGW W270, ACS, WRAS as well as NSF61 and does NOT correspond to the European food guideline EU 10/2011 as well as to the American FDA 21 CFR guideline.

Modulus

5.800MPa

Strength

100MPa

Impact

50kJ/m²

AKROMID^®

Preliminary

B3 1 S3 natural (8013)

PA6-I

AKROMID® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

AKROLOY^®

PA GF 60 black (7789)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

290MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

1 68 69 7080

AKROLOY^®

PA GF 50 black (2706)PA66+PA6I/6T GF50

AKROLOY® PA GF 50 black (2706) is a 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 50 black (6507) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

Properties

Modulus

17.500MPa

Strength

250MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

17500 MPa

16500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

250 MPa

220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

16400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

380 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

105 kJ/m²

100 kJ/m²

95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

17 kJ/m²

15 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.

290 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

225 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

245 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

243 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,15 10⁻⁴/K

0,65 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h

20.000 h

140 - 150 °C

110 - 130 °C

Vicat softening temperature B50

ISO 306

50°C/50N

242 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness

HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness

700 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,59 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,05 %

Water absorption

ISO 62

23°C, saturated

3,5 - 4 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,3 - 0,5 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.

10¹⁷ Ω

Comparative tracking index

IEC 60112

Test liquid A

600 V

Permittivity

IEC 60250

1 MHz

4,42

Rheological Properties

MVR

ISO 1133

275°C/5kg

9 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

PA GF 50 black (2706)PA66+PA6I/6T GF50

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Charpy impact strength

Charpy notched impact strength

Ball indentation hardness

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Vicat softening temperature B50

Flammability

Burning rate

GWFI

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Surface resistivity

Comparative tracking index

Permittivity

Rheological Properties

MVR

Do you have any questions? We are happy to help.

Find the right compound

PA GF 50 black (2706).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66+PA6I/6T GF50

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Charpy impact strength

Charpy notched impact strength

Ball indentation hardness

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Vicat softening temperature B50

Flammability

Burning rate

GWFI

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Surface resistivity

Comparative tracking index

Permittivity

Rheological Properties

MVR

Do you have any questions? We are happy to help.

PA GF 50 black (2706)PA66+PA6I/6T GF50