AKROLOY®

Preliminary

PA GF 40 natural (6413)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMID®

UL

B3 1 black (6528)

PA6

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

AKROMID®

B3 ICF 20 LF black (6695)

PA6 CF20

AKROMID® B3 ICF 20 LF black (6695) is a 20 % carbon fiber reinforced, conductive PA6.

Modulus

15.000MPa

Strength

175MPa

Impact

50kJ/m²

AKROMID® B3 ICF 20 LF black (6695) is a 20 % carbon fiber reinforced, conductive PA6.

PRECITE®

Preliminary

P3 GF 30 S1 natural (6853)

PBT-GF 30

PRECITE® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

Modulus

9.500MPa

Strength

135MPa

Impact

85kJ/m²

PRECITE® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

AKROMID®

Preliminary

B+ GF 30 6 LT black (7665)

PA6 GF30

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/m²

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

AKROMID®

UL

C3 GF 30 1 FR orange (7855)

PA6+PA66 GF30 FR(40)

AKROMID® C3 GF 30 1 FR orange (7855) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 2003, E&E, Public transportation EN 45545-2.

Modulus

10.600MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® C3 GF 30 1 FR orange (7855) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 2003, E&E, Public transportation EN 45545-2.

AKROMID®

Preliminary

B3 GF 30 8 black (8166)

PA6 GF30

AKROMID® B3 GF 30 8 black (8166) - PA6, 30% glass fiber, food contact, kitchen and household appliances

Modulus

10.000MPa

Strength

175MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 8 black (8166) - PA6, 30% glass fiber, food contact, kitchen and household appliances

167686980

AKROMID®

Preliminary

NEXT U28 ICF 40 1 black (8238)PA11 CF40

AKROMID® NEXT U28 ICF 40 1 black (8238) is a Polyamide 11 reinforced with 40% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure. The production of large-volume parts is possible with high throughputs > 1 kg/h in 3D-printing with pellets in screw extrusion additive manufacturing and Fused Granulate Fabrication (FGF).

Features

heat stabilised 130
recycled content
reduced density
reduced moisture
3D printing / additive manufacturing
Sports & leisure
lightweight construction

Properties

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/m²

Sustainability

Biobased carbon content

41 %

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
20000 MPa
14000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
3,7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
21000 MPa
17500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
295 MPa
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
3,3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
80 kJ/m²
75 kJ/m²
75 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
14 kJ/m²
14 kJ/m²
10 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
189 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,4 - 0,6 %

Water absorption

ISO 62

23°C, saturated
1,1 - 1,5 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.