AKROMID®

Preliminary

NEXT U3 ICF 20 1 black (8232)

PA11 CF20

AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

Modulus

9.300MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

AKROMID®

B3 GF 40 1 black (2487)

PA6 GF40

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

AKROMID®

A3 GK 30 6 natural (6774)

PA66 GB30

AKROMID® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

90MPa

Impact

25kJ/m²

AKROMID® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

AKROMID®

Preliminary

B28 GF 15 natural (6940)

PA6 GF 15

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/m²

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

AKROTEK®

Preliminary

PK-VM GF 15 8 black (6991)

PK GF15

AKROTEK® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

4.500MPa

Strength

95MPa

Impact

55kJ/m²

AKROTEK® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMID®

B3 GF 20 black (2491)

PA6 GF20

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

AKROMID®

A3 1 L natural (4800)

PA66 + PP

AKROMID® A3 1 L natural (4800) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® A3 1 L natural (4800) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

167686980

AKROMID®

Preliminary
Internal

T9 GF 15 FR LA black (8197)PPA GF15 FR(40)

AKROMID® T9 GF 15 FR LA black (8197) is a flame retardant, 15% glass fibre reinforced polyphthalamide. The product is based on PA9T and has a significantly lower moisture absorption compared to conventional PA6T grades. As a result, the glass transition area is much more constant and even in the conditioned state, the product impresses with its medium strength and stiffness. Due to its high temperature and media resistance, this material is suitable for technical components that come into contact with chemicals. The flame retardant system is free of red phosphorus and halogens. This type is laser-markable.

Features

flame retardant
laser markable

Properties

Modulus

6.000MPa

Strength

107MPa

Impact

48kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6000 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
107 MPa
101 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,2 %
2,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
48 kJ/m²
40 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
6 kJ/m²
6 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
305 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
960 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,26 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0.2 - 0.4 %
0.6 - 0.8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1014 Ω x cm
1014 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1013 Ω
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.