AKROMIDĀ®

Preliminary

B3 1 S3 natural (8013)

PA6-I

AKROMIDĀ® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

AKROMIDĀ®

Preliminary

NEXT U28 ICF 40 1 black (8238)

PA11 CF40

AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

AKROMIDĀ®

UL

A3 GF 35 1 HU natural (8418)

PA66 GF35

AKROMIDĀ® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.900MPa

Strength

216MPa

Impact

NA

AKROMIDĀ® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMIDĀ®

B3 GF 20 black (2491)

PA6 GF20

AKROMIDĀ® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/mĀ²

AKROMIDĀ® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

AKROMIDĀ®

B3 1 natural (2499)

PA6

AKROMIDĀ® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

AKROMIDĀ®

A3 GF 25 3 black (3094)

PA66 GF25

AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

Modulus

8.500MPa

Strength

160MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

AKROMIDĀ®

B3 GF 30 8 natural (5663)

PA6 GF30

AKROMIDĀ® B3 GF 30 8 natural (5663) - PA6, 30% glass fiber, food contact, kitchen and household appliances

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 30 8 natural (5663) - PA6, 30% glass fiber, food contact, kitchen and household appliances

166676880

AKROMIDĀ®

A3 GM 20/10 S1 natural (1217)PA66-I (GF20+GB10)

AKROMIDĀ® A3 GM 20/10 S1 natural (1217) is a 20% glass fiber and 10% glass beads reinforced, impact modified PA 6.6. It is characterised by a medium cold impact strength as well as good adhesion properties. Furthermore, the material impresses with a good surface appearance and low warpage and is therefore perfectly suitable for technical demanding components in the mechanical engineering and automotive industry. It has a light inherent color.

Features

impact modified
surface modified
low warpage
adhesion modified

Properties

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/mĀ²

Sustainability

Recycled content

10 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6900 MPa
4200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
130 MPa
85 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4 %
10 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6900 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
205 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
80 kJ/mĀ²
80 kJ/mĀ²
76 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
15 kJ/mĀ²
16 kJ/mĀ²
8 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
127 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,27 10ā»ā“/K
1,11 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,31 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2 %

Water absorption

ISO 62

23Ā°C, saturated
5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,4 - 0,6 %
0,9 - 1,1 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more