PRECITE®
K GF 15 natural (7439)
PBT-PET- GF 15
PRECITE K GF 15 natural (7439) is a 15% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.
6.000MPa
115MPa
30kJ/m²
PRECITE K GF 15 natural (7439) is a 15% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.
AKROMID®
NEXT G3 GF 30 1 L CI natural (8377)
PA6.9 + PP GF30
AKROMID® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
8.000MPa
125MPa
65kJ/m²
AKROMID® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
AKROMID®
NEXT U3 ICF 20 1 black (8232)
PA11 CF20
AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
9.300MPa
110MPa
60kJ/m²
AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
AKROMID®
A3 GF 35 1 HU natural (8418)
PA66 GF35
AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
11.900MPa
216MPa
NA
AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
AKROMID®
B3 GF 60 natural (2476)
PA6 GF60
AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color
21.000MPa
240MPa
90kJ/m²
AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color
AKROMID®
B3 GF 25 natural (2471)
PA6 GF25
AKROMID® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color
8.500MPa
160MPa
85kJ/m²
AKROMID® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color
AKROMID®
B3 GF 60 black (2497)
PA6 GF60
AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength
21.000MPa
240MPa
90kJ/m²
AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength
AKROMID®
B28 GF 30 S3 natural (8348)PA6-I GF30
AKROMID® B28 GF 30 S3 natural (8348) is a 30% glass fibre reinforced, easy flowing polyamide 6. Furthermore, the material is impact modified and therefore characterised by a higher dry impact strength compared to standard PA 6 GF 30. Its high strength and stiffness make it the material of your choice for technical applications in industrial engineering and in the furniture industry. The material has a light inherent color.
Features
Properties
8.900MPa
160MPa
100kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.