AKROMID®

Preliminary

NEXT B3 GF 30 1 L CI black (8375)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

AKROLEN®

Preliminary

PP LGF 40 2 black (8488)

PP LGF40

AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

AKROMID®

Preliminary

T91 GF 30 FR black (8184)

PPA GF30 FR(40)

AKROMID® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

Modulus

11.000MPa

Strength

140MPa

Impact

40kJ/m²

AKROMID® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

AKROMID®

Preliminary

B3 GKM 40 natural (8630)

PA6 M40

AKROMID® B3 GKM 40 natur (8630) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

Modulus

4.900MPa

Strength

70MPa

Impact

150kJ/m²

AKROMID® B3 GKM 40 natur (8630) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

AKROMID®

A3 1 S3 black (1139)

PA66-I

AKROMID® A3 1 S3 black (1139) - PA 6.6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (1139) - PA 6.6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMID®

B3 GK 15 natural (1824)

PA6 GB15

AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

Modulus

4.000MPa

Strength

85MPa

Impact

30kJ/m²

AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

AKROMID®

B3 natural (1024)

PA6

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

Modulus

3.200MPa

Strength

83MPa

Impact

180kJ/m²

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

162636480

AKROMID®

Internal

S3 GF 50 1 natural (3533)PA610 GF50

AKROMID® S3 GF 50 1 natural (3533) is a 50% glass fibre reinforced, heat stabilised polyamide 6.10 with very high stiffness and strength as well as lower moisture absorption, high chemical resistance and light inherent color.

Features

heat stabilised 130
reduced moisture

Properties

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

61 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14500 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
310 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
105 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
20 kJ/m²
16 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,51 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more