AKROMID®
A28 GF 40 1 natural (4919)
PA66 GF40
AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
13.000MPa
245MPa
95kJ/m²
AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
A3 ICF 15 black (5056)
PA66 CF15
AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
12.000MPa
170MPa
45kJ/m²
AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROMID®
T9 GF 15 S1 black (7820)
PPA-I GF15
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
5.000MPa
120MPa
73kJ/m²
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
B3 GF 35 1 HU black (8413)
PA6 GF35
AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
11.500MPa
195MPa
100kJ/m²
AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
AKROMID®
B3 GF 15 1 L natural (4690)
PA6+PP GF15
AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
5.200MPa
110MPa
60kJ/m²
AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
AKROMID®
B3 ICF 20 black (5103)
PA6 CF20
AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
13.500MPa
150MPa
55kJ/m²
AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
AKROLEN®
PP LGF 40 2 black (8488)
PP LGF40
AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.
10.100MPa
140MPa
81kJ/m²
AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.
AKROMID®
B3 GF 30 FR black (8883)PA6 GF30 FR(40)
AKROMID® B3 GF 30 FR black (8883) is a 30 % glass fiber reinforced, flame-retardant PA6 in black. Listed to UL 94 in all colors, the material is based on a flame retardant system that is free of red phosphorus, halogens, melamine and PFAS. The product is also aniline-free. An improved surface quality is achieved through good flowability. This grade is particularly suitable for applications with high strength requirements in the automotive and E&E markets.
Features
Regulatory
Properties
10.800MPa
135MPa
65kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Ball pressure test
IEC 60695-10-2
Flammability
Burning rate
UL 94
Burning rate 5V
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
HWI
UL 746A
HAI
UL 746A
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Dielectric strength
IEC 60243
Inclined-Plane Tracking, IPT
ASTM D2303-13
High voltage arc tracking rate (HVTR)
UL 746A
High Volt, Low Current Arc Resistance
ASTM D495
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.