Select your fitting and find the right compound for your intend
AKROMID®
B3 3 natural (5772)
PA6
AKROMID® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland
3.200MPa
80MPa
NA
AKROMID® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland
AKROMID®
T9 GF 15 S1 black (7820)
PPA-I GF15
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
5.000MPa
120MPa
73kJ/m²
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
T9 GF 35 4 black (7858)
PPA GF35
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
11.000MPa
200MPa
75kJ/m²
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLEN®
PP LGF 40 2 black (8488)
PP LGF40
AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.
10.100MPa
140MPa
81kJ/m²
AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.
AKROMID®
A3 1 S3 grey (2955)
PA66+PA6-I
AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.500MPa
68MPa
180kJ/m²
AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
AKROMID®
NEXT B3 GF 30 1 L CI black (8375)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
T91 GF 30 FR black (8184)
PPA GF30 FR(40)
AKROMID® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.
11.000MPa
140MPa
40kJ/m²
AKROMID® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.
AKROMID®
AKROMID® C28 GF 25 FRT grey (8133) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend, colored in grey similar to RAL 7011. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications and certified to EN 45545-2 R6 and EN 45545-2 R1. To achieve an excellent surface quality a mould temperature of at least 120°C is necessary.
Features
Regulatory
Properties
11.000MPa
150MPa
Na
ISO 527-2
ISO 527-2
ISO 527-2
ISO 11357-3
UL 94
IEC 60695-2-12
IEC 60695-2-13
FMVSS 302
EN 45545-2
ISO 1183
ISO 1110
ISO 294-4
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.