AKROMIDĀ®
B3 3 natural (5772)
PA6
AKROMIDĀ® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland
3.200MPa
80MPa
NA
AKROMIDĀ® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland
AKROMIDĀ®
T9 GF 15 S1 black (7820)
PPA-I GF15
AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
5.000MPa
120MPa
73kJ/mĀ²
AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
T9 GF 35 4 black (7858)
PPA GF35
AKROMIDĀ® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
11.000MPa
200MPa
75kJ/mĀ²
AKROMIDĀ® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLENĀ®
PP LGF 40 2 black (8488)
PP LGF40
AKROLENĀ® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.
10.100MPa
140MPa
81kJ/mĀ²
AKROLENĀ® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.
AKROMIDĀ®
A3 1 S3 grey (2955)
PA66+PA6-I
AKROMIDĀ® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.500MPa
68MPa
180kJ/mĀ²
AKROMIDĀ® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
AKROMIDĀ®
NEXT B3 GF 30 1 L CI black (8375)
PA6 + PP GF30
AKROMIDĀ® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/mĀ²
AKROMIDĀ® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMIDĀ®
T91 GF 30 FR black (8184)
PPA GF30 FR(40)
AKROMIDĀ® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.
11.000MPa
140MPa
40kJ/mĀ²
AKROMIDĀ® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.
AKROMIDĀ®
T9 GF 15 S1 black (7820)PPA-I GF15
AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
Features
Properties
5.000MPa
120MPa
73kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Glass transition temperature
ISO 11357-2
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.