AKROMID®

B3 GF 50 black (2939)

PA6 GF50

AKROMID® B3 GF 50 black (2939) - 50% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (2939) - 50% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMID®

Preliminary

A3 GF 30 4 natural (3752)

PA66 GF30

AKROMID® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

11.500MPa

Strength

210MPa

Impact

100kJ/m²

AKROMID® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color

AKROMID®

B3 GF 30 S1 white (3767)

PA6-I GF30

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

160MPa

Impact

105kJ/m²

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROLOY®

PA GF 50 grey (3807)

PA66 + PA6I/6T GF50

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

Modulus

17.200MPa

Strength

250MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

AKROMID®

A3 ICF 15 black (5056)

PA66 CF15

AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

12.000MPa

Strength

170MPa

Impact

45kJ/m²

AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

B3 GF 15 8 L natural (5689)

PA6+PP GF15

AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011

Modulus

5.200MPa

Strength

110MPa

Impact

65kJ/m²

AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011

AKROMID®

B3 GF 35 1 black (20017)

PA6 GF35

AKROMID® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

185MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

160616280

AKROMID®

UL

NEXT S3 GF 30 1 HU black (8825)PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) is a partially biobased and heat-stabilised PA6.10. With 30% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This sustainable and UL listed grade is characterised by its low moisture absorption and high chemical resistance compared to classic PA6 and PA 6.6.

Features

Bio-based
heat stabilised 130
reduced moisture

Regulatory

ul

Properties

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

59 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8600 MPa
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
7,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
5,5 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
17 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
195 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
145 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 - 1,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,8 - 1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more