AKROMID®
T9 GF 15 S1 black (7820)
PPA-I GF15
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
5.000MPa
120MPa
73kJ/m²
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
B3 GF 35 1 HU black (8413)
PA6 GF35
AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
11.500MPa
195MPa
100kJ/m²
AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
AKROMID®
B3 GF 25 1 natural (2463)
PA6 GF25
AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color
8.500MPa
160MPa
85kJ/m²
AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color
AKROMID®
B3 GF 10 natural (2829)
PA6 GF10
AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.
4.800MPa
105MPa
47kJ/m²
AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.
AKROMID®
A3 GF 30 4 natural (3752)
PA66 GF30
AKROMID® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color
11.500MPa
210MPa
100kJ/m²
AKROMID® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color
AKROMID®
NEXT B3 GF 30 1 L CI black (8375)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
A3 1 S3 grey (2955)
PA66+PA6-I
AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.500MPa
68MPa
180kJ/m²
AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
AKROMID®
B28 GF 30 9 FR grey (8505)PA6 GF30 FR(40)
AKROMID® B28 GF 30 9 FR grey (8505) is a flame retardant PA6 with 30% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade is UL listed with a V0 classification at 1.6mm. Due to its very good flowability, it is characterised by easy processability as well as good surface properties. The material has excellent long-term thermal stability and outstanding mechanical properties. The colour is slightly darker than RAL 7035.
Features
Regulatory
Properties
11.000MPa
135MPa
80kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Temperature index for 50% loss of tensile strength
IEC 60216
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Dielectric strength
IEC 60243
Inclined-Plane Tracking, IPT
ASTM D2303-13
High voltage arc tracking rate (HVTR)
UL 746A
High Volt, Low Current Arc Resistance
ASTM D495
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.