AKROMID®
A3 GF 13 S3 natural (2788)
PA66-I GF13
AKROMID® A3 GF 13 S3 natural (2788) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry
5.200MPa
125MPa
75kJ/m²
AKROMID® A3 GF 13 S3 natural (2788) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry
AKROMID®
A3 1 FR black (3051)
PA66 FR(30)
AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.
3.500MPa
83MPa
70kJ/m²
AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.
AKROMID®
B3 ICF 20 black (5103)
PA6 CF20
AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
13.500MPa
150MPa
55kJ/m²
AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
AKROMID®
B3 GF 15 8 L natural (5689)
PA6+PP GF15
AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011
5.200MPa
110MPa
65kJ/m²
AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011
AKROMID®
T9 GF 35 4 black (7858)
PPA GF35
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
11.000MPa
200MPa
75kJ/m²
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
B3 GF 35 1 HU black (8413)
PA6 GF35
AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
11.500MPa
195MPa
100kJ/m²
AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.
AKROMID®
B3 GF 10 natural (2829)
PA6 GF10
AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.
4.800MPa
105MPa
47kJ/m²
AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.
AKROTEK®
PK-HM natural (7536)PK
PK-HM natural (7536) is an unreinforced, purified Polyketone with average flowability. The outstanding friction and wear properties enable the use for demanding components exposed to tribological stress. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. This grade is especially designed for extrusion process.
Features
Properties
1.400MPa
60MPa
180kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at yield
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.