AKROMID®

Preliminary

T9 GF 15 S1 black (7820)

PPA-I GF15

AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Modulus

5.000MPa

Strength

120MPa

Impact

73kJ/m²

AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

AKROMID®

UL

B3 GF 35 1 HU black (8413)

PA6 GF35

AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMID®

B3 GF 25 1 natural (2463)

PA6 GF25

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

AKROMID®

B3 GF 10 natural (2829)

PA6 GF10

AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.

Modulus

4.800MPa

Strength

105MPa

Impact

47kJ/m²

AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.

AKROMID®

Preliminary

A3 GF 30 4 natural (3752)

PA66 GF30

AKROMID® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

11.500MPa

Strength

210MPa

Impact

100kJ/m²

AKROMID® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color

AKROMID®

Preliminary

NEXT B3 GF 30 1 L CI black (8375)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

AKROMID®

A3 1 S3 grey (2955)

PA66+PA6-I

AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.500MPa

Strength

68MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

160616280

AKROMID®

A3 GF 50 4 black (7282)PA66 GF50

AKROMID® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

Features

heat stabilised 160
hydrolysis / chemically stabilised

Properties

Modulus

17.000MPa

Strength

250MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17000 MPa
13000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
180 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,0 %
4,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
15500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
380 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
110 kJ/m²
115 kJ/m²
110 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
20 kJ/m²
25 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
160 °C

General properties

Density

ISO 1183

23°C
1,57 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,5 %

Water absorption

ISO 62

23°C, saturated
3,7 - 4,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more