AKROMID®

B3 GF 50 black (2939)

PA6 GF50

AKROMID® B3 GF 50 black (2939) - 50% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (2939) - 50% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMID®

Preliminary

A3 GF 30 4 natural (3752)

PA66 GF30

AKROMID® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

11.500MPa

Strength

210MPa

Impact

100kJ/m²

AKROMID® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color

AKROMID®

B3 GF 30 S1 white (3767)

PA6-I GF30

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

160MPa

Impact

105kJ/m²

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROLOY®

PA GF 50 grey (3807)

PA66 + PA6I/6T GF50

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

Modulus

17.200MPa

Strength

250MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

AKROMID®

A3 ICF 15 black (5056)

PA66 CF15

AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

12.000MPa

Strength

170MPa

Impact

45kJ/m²

AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

B3 GF 15 8 L natural (5689)

PA6+PP GF15

AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011

Modulus

5.200MPa

Strength

110MPa

Impact

65kJ/m²

AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011

AKROMID®

B3 GF 35 1 black (20017)

PA6 GF35

AKROMID® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

185MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

160616280

AKROLOY®

PA GF 50 natural (2916)PA66+PA6I/6T GF50

AKROLOY® PA GF 50 natural (2916) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 50 natural (6414) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

Properties

Modulus

17.500MPa

Strength

250MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17500 MPa
16500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
16400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
380 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
105 kJ/m²
100 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
17 kJ/m²
17 kJ/m²
15 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
290 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
225 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,15 10⁻⁴/K
0,65 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
140 - 150 °C
110 - 130 °C

Vicat softening temperature B50

ISO 306

50°C/50N
242 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,59 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,4 %

Water absorption

ISO 62

23°C, saturated
3,5 - 4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,0 - 0,2 %
0,3 - 0,5 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1017 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Permittivity

IEC 60250

1 MHz
4,42

Rheological Properties

MVR

ISO 1133

275°C/5kg
9 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more