Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 GF 15 1 L natural (4690)

PA6+PP GF15

AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMID®

B3 ICF 20 black (5103)

PA6 CF20

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMID®

A3 ICF 15 black (5056)

PA66 CF15

AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

12.000MPa

Strength

170MPa

Impact

45kJ/m²

AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROLOY®

PA GF 50 grey (3807)

PA66 + PA6I/6T GF50

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

Modulus

17.200MPa

Strength

250MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

PRECITE®

Preliminary

K GF 30 natural (7437)

PBT-PET- GF 30

PRECITE® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

Modulus

10.800MPa

Strength

170MPa

Impact

60kJ/m²

PRECITE® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

AKROLEN®

Preliminary

PP LGF 40 2 black (8488)

PP LGF40

AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

AKROMID®

Preliminary

NEXT B3 GF 30 1 L CI black (8375)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

159606180

AKROTEK®

Preliminary

PK-VM GF 15 natural (8680)PK GF15

AKROTEK® PK-VM GF 15 natural (8680) is a 15% glass fibre reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 15 natur (4705) in order to meet the requirements for a larger processing window during processing.

Features

hydrolysis / chemically stabilised

Properties

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
4600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
130 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
10 kJ/m²
10 kJ/m²
7 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
119 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,35 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,5 - 0,7 %
1,1 - 1,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more