AKROMID®

B3 GF 20 1 black (2483)

PA6 GF20

AKROMID® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

AKROMID® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength

AKROMID®

B3 ICF 20 black (5103)

PA6 CF20

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMID®

B3 GF 15 8 L natural (5689)

PA6+PP GF15

AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011

Modulus

5.200MPa

Strength

110MPa

Impact

65kJ/m²

AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011

AKROMID®

A3 GF 13 S3 natural (2788)

PA66-I GF13

AKROMID® A3 GF 13 S3 natural (2788) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

Modulus

5.200MPa

Strength

125MPa

Impact

75kJ/m²

AKROMID® A3 GF 13 S3 natural (2788) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

AKROMID®

UL

A3 1 FR black (3051)

PA66 FR(30)

AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

Modulus

3.500MPa

Strength

83MPa

Impact

70kJ/m²

AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

AKROMID®

B3 GF 30 S1 white (3767)

PA6-I GF30

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

160MPa

Impact

105kJ/m²

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

A3 GF 25 FR natural (7649)

PA66 GF25 FR(40)

AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

9.200MPa

Strength

135MPa

Impact

63kJ/m²

AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

159606180

AKROTEK®

Preliminary

PK-VM GF 40 8 black (6995)PK GF40

AKROTEK® PK-VM GF 40 8 black (6995) is a 40% glass fibre reinforced polyketone with high stiffness and strength. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances. Please note that the material is NOT suitable anymore for drinking water contact and does NOT meet the requirements according to KTW, DVGW W270, ACS, WRAS as well as NSF61.

Features

hydrolysis / chemically stabilised

Regulatory

eu102011fda

Properties

Modulus

11.000MPa

Strength

150MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
2,3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
50 kJ/m²
40 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
16 kJ/m²
16 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,56 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,5 - 0,6 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.