Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
B3 GF 50 S1 natural (3694)
PA6-I GF50
AKROMID® B3 GF 50 S1 natural (3694) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
14.500MPa
190MPa
110kJ/m²
AKROMID® B3 GF 50 S1 natural (3694) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
AKROMID®
B3 GF 15 1 L natural (4690)
PA6+PP GF15
AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
5.200MPa
110MPa
60kJ/m²
AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
AKROMID®
B3 GF 15 8 L natural (5689)
PA6+PP GF15
AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011
5.200MPa
110MPa
65kJ/m²
AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011
AKROMID®
B3 1 L black (4525)
PA6+PP
AKROMID® B3 1 L schwarz (4525) - PA/PP-Blend lightweight, cost reduced
2.300MPa
55MPa
180kJ/m²
AKROMID® B3 1 L schwarz (4525) - PA/PP-Blend lightweight, cost reduced
AKROMID®
B3 3 natural (5772)
PA6
AKROMID® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland
3.200MPa
80MPa
NA
AKROMID® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland
AKROLOY®
PA GF 40 black (2845)
PA66 + PA6I/6T GF40
AKROLOY® PA GF 40 black (2845) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 40 black (6416) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
13.000MPa
230MPa
95kJ/m²
AKROLOY® PA GF 40 black (2845) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 40 black (6416) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
AKROMID®
T9 GF 15 S1 black (7820)
PPA-I GF15
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
5.000MPa
120MPa
73kJ/m²
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
C3 GF 25 1 FR grey (8803) PA66+PA6 GF25 FR(40)
AKROMID® C3 GF 25 1 FR grey (8803) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend, colored in grey, similar to RAL 7035 with good lasermarkability. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable for high voltage components in e-mobility.
Features
Regulatory
Properties
9.100MPa
120MPa
46kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
RTI electrical
UL 746B
RTI impact
UL 746B
RTI strength
UL 746B
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Dielectric strength
IEC 60243
High voltage arc tracking rate (HVTR)
UL 746A
High Volt, Low Current Arc Resistance
ASTM D495
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.