PRECITEĀ®

Preliminary

K GF 30 natural (7437)

PBT-PET- GF 30

PRECITEĀ® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

Modulus

10.800MPa

Strength

170MPa

Impact

60kJ/mĀ²

PRECITEĀ® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

AKROMIDĀ®

A3 GF 25 FR natural (7649)

PA66 GF25 FR(40)

AKROMIDĀ® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

9.200MPa

Strength

135MPa

Impact

63kJ/mĀ²

AKROMIDĀ® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

AKROMIDĀ®

UL

A3 1 FR black (3051)

PA66 FR(30)

AKROMIDĀ® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

Modulus

3.500MPa

Strength

83MPa

Impact

70kJ/mĀ²

AKROMIDĀ® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

AKROMIDĀ®

A3 GF 30 4 black (3571)

PA66 GF30

A3 GF 30 4 black (3571) - PA 6.6 30% glass fiber reinforced, hydrolysis and chemically stabilised, suitable for cooling systems in the automotive industry

Modulus

11.500MPa

Strength

210MPa

Impact

80kJ/mĀ²

A3 GF 30 4 black (3571) - PA 6.6 30% glass fiber reinforced, hydrolysis and chemically stabilised, suitable for cooling systems in the automotive industry

AKROMIDĀ®

S3 8 natural (4881)

PA610

AKROMIDĀ® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact

Modulus

2.300MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact

AKROMIDĀ®

A3 1 S3 grey (2955)

PA66+PA6-I

AKROMIDĀ® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.500MPa

Strength

68MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMIDĀ®

Preliminary

NEXT B3 GF 30 1 L CI black (8375)

PA6 + PP GF30

AKROMIDĀ® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/mĀ²

AKROMIDĀ® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

158596080

AKROTEKĀ®

PK-VM GF 30 black (8655)PK GF30

AKROTEKĀ® PK-VM GF 30 black (8655) is a 30% glass fiber reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. The material can be laser marked. This type was developed as the successor to PK-VM GF 30 black (4896) in order to meet the requirements for a larger processing window during processing.

Features

hydrolysis / chemically stabilised
E-Mobility

Properties

Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8500 MPa
8200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
130 MPa
130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,0 %
3,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
210 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
70 kJ/mĀ²
75 kJ/mĀ²
70 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
11 kJ/mĀ²
14 kJ/mĀ²
11 kJ/mĀ²
10 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,18 10ā»ā“/K
1,16 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
725 Ā°C
725 Ā°C

HWI

UL 746A

1,6 mm Wall thickness
1 PLC

General properties

Density

ISO 1183

23Ā°C
1,48 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,6 - 0,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Rheological Properties

MVR

ISO 1133

240Ā°C/2,16kg
4 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more